Thickness-Dependent Raman and Photoluminescence Spectra of 2D Indium Selenide

Simple item page
dc.contributor.authorNemkayeva, Renata
dc.contributor.authorGuseinov, Nazim
dc.contributor.authorBaigarinova, Gulzhan
dc.contributor.authorAitzhanov, Madi
dc.contributor.authorMukhametkarimov, Yerzhan
dc.date.accessioned2020-11-04T11:21:44Z
dc.date.available2020-11-04T11:21:44Z
dc.date.issued2020-08
dc.description.abstractRecently, III–VI group layered two-dimensional (2D) semiconductors, such as GaS, GaSe, InSe, have considered as promising potential materials for next-generation optoelectronic devices, due to their variable bandgap, high electron mobility, wide photoluminescence (PL) response and ohmic contact [1-3]. In this work, samples of layered indium selenide were synthesized by fusing the corresponding stoichiometric compositions in a vacuum and then thinned down to a nanometer thickness using micromechanical exfoliation. Obtained thin flakes of InSe were placed on SiO2/Si substrates and studied using atomic-force microscopy and Raman spectroscopy. It was found out that the decrease of the thickness down to 4 nm leads to the rise of an additional peak at ~200 cm-1 in Raman spectrum, which is explained by mechanical stress or by the stronger light absorption of thinner InSe flakes. Photoluminescence studies were performed using Raman spectrometer and 473 nm excitation laser. There was revealed a strong dependence of the intensity of PL peak at 510 nm (2.43 eV) on the thickness of the InSe flake. However, single- and bi-layered samples demonstrate neither Raman nor PL signal, possibly due to the fast oxidation without protective coating.en_US
dc.identifier.urihttp://nur.nu.edu.kz/handle/123456789/5070
dc.language.isoenen_US
dc.publisherThe 8th International Conference on Nanomaterials and Advanced Energy Storage Systems; Nazarbayev University; National Laboratory Astana; Institute of Batteriesen_US
dc.rightsAttribution-NonCommercial-ShareAlike 3.0 United States*
dc.rights.urihttp://creativecommons.org/licenses/by-nc-sa/3.0/us/*
dc.subjecttwo-dimensional semiconductorsen_US
dc.subjectohmic contacten_US
dc.subjectindium selenideen_US
dc.subjectResearch Subject Categories::TECHNOLOGYen_US
dc.titleThickness-Dependent Raman and Photoluminescence Spectra of 2D Indium Selenideen_US
dc.typeAbstracten_US
workflow.import.sourcescience

Files

Original bundle
Now showing 1 - 1 of 1
Thumbnail Image
Name:
Abstract book INESS 2020.page59.pdf
Size:
332.21 KB
Format:
Adobe Portable Document Format
Description:
Abstract
Download
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
6.28 KB
Format:
Item-specific license agreed upon to submission
Description:
Download

Collections

Abstracts